New insight could lead to better silicon solar panels

solar panel
Credit: CC0 Public Domain

Researchers at the U.S. Department of Energy's National Renewable Energy Laboratory (NREL) and Colorado School of Mines are applying a new technique to identify defects in silicon solar cells that cause a drop in efficiency. The lessons learned at the atomic level could lead to improvements in the way manufacturers strengthen their products against what is known as light-induced degradation.

Light-induced degradation, or LID, shaves the efficiency of silicon by about 2%, which adds up to a significant drop in power output over the 30- to 40-year lifespan of the technology deployed in the field. Solar made from silicon account for more than 96% of the , and the most commonly used semiconductor used in the manufacture of these cells is made from boron-doped silicon. But boron-doped silicon is susceptible to LID, so manufacturers have developed methods to stabilize the solar modules.

Without an understanding of the defects at the , the researchers said it is impossible to predict the stability of those modules.

"Some of the modules are stabilized completely. Some of them are only half-stabilized," said Abigail Meyer, a Ph.D. candidate at Mines and a researcher at NREL. She is the lead author of a new paper detailing efforts to pinpoint the source of the LID phenomenon. The article, "Atomic Structure of Light-Induced Efficiency-Degrading Defect in Boron-Doped Czochralski Silicon Solar Cells," appears in the journal Energy & Environmental Science.

Her co-authors are Vincenzo LaSalvia, William Nemeth, Matthew Page, David Young, Paul Stradins, all from NREL; Sumit Agarwal, Michael Venuti, and Serena Eley, who are from Mines; and P. Craig Taylor, a retired Mines professor who consulted on the research.

Stradins, a principal scientist and a project leader in silicon photovoltaic research at NREL, said the problem of LID has been studied for decades but the exact microscopic nature of what causes the degradation has not been determined. Researchers have concluded, through indirect experimentation and theory, that the problem decreases when less boron is used or when less oxygen is present in the silicon.

The collaboration between NREL and Mines researchers relied on electron paramagnetic resonance (EPR) to identify defects responsible for the LID. For the first time, the revealed a distinct defect signature as the sample solar cells became more degraded by light. The signature disappeared when the scientists applied the empirical "regeneration" process to cure the LID that industry has adopted. To their surprise, the researchers also found a second, "broad" EPR signature affected by light exposure, involving many more dopant atoms than there are LID defects. They hypothesized that not all atomic changes induced by light lead to the LID.

The techniques developed to study LID can be extended to reveal other types of degrading defects in solar cells and in other semiconductor materials used in photovoltaics including cadmium telluride and perovskites, the scientists noted.


Explore further

The sunlight that powers solar panels also damages them: 'Gallium doping' is providing a solution

More information: Abigail R. Meyer et al, Atomic structure of light-induced efficiency-degrading defects in boron-doped Czochralski silicon solar cells, Energy & Environmental Science (2021). DOI: 10.1039/D1EE01788H
Journal information: Energy & Environmental Science

Citation: New insight could lead to better silicon solar panels (2021, October 19) retrieved 6 December 2021 from https://techxplore.com/news/2021-10-insight-silicon-solar-panels.html
This document is subject to copyright. Apart from any fair dealing for the purpose of private study or research, no part may be reproduced without the written permission. The content is provided for information purposes only.
1732 shares

Feedback to editors