A 20 kW laser system for producing high-purity crystals

20 kW laser system for producing high-purity crystals
Gallium oxide crystals are produced in Japan with a 20 kW diode laser using the high-power optical system of the Fraunhofer ILT. Credit: Fraunhofer ILT, Aachen, Germany

High-purity semiconductor crystals are required for power electronics in electric cars or in photovoltaics. When such crystals reach a diameter of 2 inches, they become relevant for industrial applications.

Researchers from Japan and Germany have now developed a method to produce such crystals using a laser-based process, and without a crucible. The team at the Fraunhofer Institute for Laser Technology ILT in Aachen has developed a process-adapted optical system for use with a 20 kW laser.

The advantages of the laser-diode floating zone (LDFZ) process

In modern electrical engineering, relatively must be switched quickly. To accomplish this, the electronics are based on wide-bandgap semiconductors such as gallium oxide (Ga2O3). Since it has a of about 1,800 °C and is grown from the melt, this material is easier to produce than other wide-bandgap semiconductors such as (SiC) or gallium nitride (GaN), both of which are grown using chemical vapor deposition.

To date, crucible-based methods such as the Czochralski and the edge-defined film-fed growth (EFG) processes have mainly been used to produce gallium oxide crystals. However, the purity of the crystal is limited by the diffusion of the crucible material.

Contamination of the melt can be avoided by supplying the heat in the form of radiation, rather than via the crucible, which causes the polycrystalline starting material to be remelted into a high-purity . Of course, this can also be achieved with heating lamps. In contrast to heating lamps, however, the emission of the laser not only has long-term stability, but the laser also only emits its radiation in one direction, which means that the heat input is much more targeted.

In addition, the laser beam profile can be optimized with regard to the heating process. The possible crystal diameters scale with the heating power, so increasingly powerful laser systems have been used for the laser-diode floating zone (LDFZ) process in recent years.

The optics matter

Using laser powers of more than 5 kW for growing crystals is new; until now, comparable powers have been used in established laser material processing methods such as cutting and welding. The for this have to be designed and cooled carefully, as even small losses of less than 1% can lead to their destruction during prolonged use.

Fraunhofer ILT in Aachen has, therefore, developed a water-cooled high-performance optical system, especially for the LDFZ process. With it, the radiation emitted by the laser is initially split into five partial beams with a maximum of 4 kW each. The partial beams are then deflected via large, water-cooled mirrors in such a way that they heat the crystal in the center of the setup evenly, offset by exactly 72°.

The optics were set up and characterized in Aachen and then transferred to the project partners in Japan. They were installed in compliance with pandemic regulations, and Aachen project manager Dr. Martin Traub is satisfied. "Commissioning via video conference was a real novelty, but it worked well. The test phase was successful and the system was operated reliably until the planned end of the project."

Cutting-edge German-Japanese research

Project partner Dr. Toshimitsu Ito from the National Institute of Advanced Industrial Science and Technology (AIST) in Tsukuba Science City in Japan has already gained a great deal of experience with the LDFZ process. The institute was able to produce gallium oxide crystals with a diameter of up to 12 mm at lower powers.

With the new 20 kW system, it should be possible to significantly increase the diameter. After commissioning and initial tests to melt the gallium oxide raw material, AIST carried out crystal growth experiments with the new LDFZ system.

The results of these investigations will be published shortly, but this much can already be said, The project partners succeeded in growing crystals with a diameter of up to 30 mm—the largest crystals ever produced using a crucible-free growth process.

Provided by Fraunhofer-Institut für Lasertechnik ILT
Citation: A 20 kW laser system for producing high-purity crystals (2024, February 9) retrieved 1 March 2024 from
This document is subject to copyright. Apart from any fair dealing for the purpose of private study or research, no part may be reproduced without the written permission. The content is provided for information purposes only.